17-4PH / SUS630 Roestvrijstalen staaf
| DIN | ASTM | AISI | UNS | JIS | Andere |
| 1.4542 | |||||
| X5CrNiCuNb16-4 | Rang 630 | 630 | S17400 | SUS 630 | 17-4PH |
| AMS 5643 | |||||
| AMS 5622 | |||||
| Z6CNU17-04 | |||||
| 10705GU-GV |
Chemische samenstelling ( %)
| C | Si | Mn | P. | S | Cr | Ni | Ma | Andere |
|---|---|---|---|---|---|---|---|---|
| ≤ 0,07 | ≤ 1,00 | ≤ 1,00 | ≤ 0,040 | ≤ 0,030 | 15,0 ～ 17,0 | 3,00 ～ 5,00 | - | Cu 3,00 ～ 5,00 Nb + Ta 0,15 - 0,45 |
Mechanische eigenschappen
| Staat van warmtebehandeling | Treksterkte Rm (MPa) | Opbrengst Rp0,2 (MPa) | Verlenging EEN(%) | Vermindering van kruis sectie over breuk Z (%) | Gevolg AKV / AKU (J) | Brinell Hardheid (HBW) |
|---|---|---|---|---|---|---|
| Onthard | ≤ 1034 | ≤ 650 | 6,0 ～ 15,0 | 30,0 ～ 60,0 | - | ≤ 363 |
| H900 | ≥ 1380 | ≥ 1275 | ≥ 14,0 | ≥ 50,0 | ≥ 20 | ≤ 420 |
| H925 | ≥ 1310 | ≥ 1200 | ≥ 14,0 | ≥ 54,0 | ≥ 34 | ≤ 409 |
| H1025 | ≥ 1170 | ≥ 1140 | ≥ 15,0 | ≥ 56,0 | ≥ 47 | ≤ 352 |
| H1075 | ≥ 1140 | ≥ 1035 | ≥ 16,0 | ≥ 58,0 | ≥ 61 | ≤ 341 |
| H1100 | ≥ 1035 | ≥ 930 | ≥ 17,0 | ≥ 58,0 | ≥ 61 | ≤ 332 |
| H1150 | ≥ 1000 | ≥ 860 | ≥ 19,0 | ≥ 60,0 | ≥ 68 | ≤ 311 |
| H1150 + H1150 | ≥ 965 | ≥ 760 | ≥ 20,0 | ≥ 60,0 | ≥ 108 | ≤ 302 |
| H1150M | ≥ 860 | ≥ 585 | ≥ 22,0 | ≥ 68,0 | ≥ 135 | ≤ 277 |
Vormen en vormen:
Ronde staaf (diameter): 5,5 mm tot 700 mm
Walsdraad (diameter): 0,10 ~ 16 mm
Vierkante staaf / Vlakke staaf: 5 mm tot 550 mm
Staalband via koudgewalst: T0.1 - 3 mm X W5 - 650 mm XL (of in rolvorm)
Gesmede ring: OD200 ~ 1500 mm X ID150 ~ 1250 mm X H20 ~ 1250 mm
Zware / middelste plaat via warmgewalst: T50 - 200 mm X B80- 1200 mm X L1000-3000 mm
Smeedstuk: trapassen met flanken / schijven / buizen / slakken / donuts / blokjes / andere verschillende vormen op basis van OEM.
Lengte: vaste lengte of willekeurige lengte of op basis van de speciale eisen van de klant.